Product: 4.8mm ID to 2.4mm ID 1.2m Lengths
Heat Shrink – RSFR-DR Diesel Fuel, Chemical, and Abrasion Resistant Tubing
Applications:
Cable harnesses in vehicles, formulated for optimum high temperature and fluid resistance.
General:
- Shrink ratio 2:1
- Flame retarded and self extinguishing
- Dielectric strength 15kV/mm
- Resistance to chemical, diesel fuels, hydraulic fluids and lubricating oils
- Operating temperature range -75°C to +150°C
- Meets AMS-DTL-23053/1
All Dim mm Part Number |
As Supplied | After Recovery | Applicable Range |
||
Inside Ø | Inside Ø | Wall | |||
RSFR-DR3.2 | 3.2 | ≤ 1.60 | 0.76 ± 0.15 | 1.1 ~ 3.0 Ø | |
RSFR-DR4.8 | 4.8 | ≤ 2.40 | 0.84 ± 0.15 | 1.7 ~ 4.4 Ø | |
RSFR-DR6.4 | 6.4 | ≤ 3.20 | 0.89 ± 0.15 | 1.3 ~ 6.1 Ø | |
RSFR-DR9.5 | 9.5 | ≤ 4.80 | 1.02 ± 0.20 | 3.4 ~ 9.1 Ø | |
RSFR-DR12.7 | 12.7 | ≤ 6.40 | 1.22 ± 0.20 | 4.4 ~ 12.2 Ø | |
RSFR-DR19.1 | 19.1 | ≤ 9.50 | 1.45 ± 0.28 | 6.5 ~ 18.7 Ø | |
RSFR-DR25.4 | 25.4 | ≤ 12.70 | 1.78 ± 0.28 | 8.8 ~ 24.8 Ø | |
RSFR-DR38.1 | 39.0 | ≤ 19.00 | 2.41 ± 0.41 | 13.8 ~ 38.4 Ø | |
RSFR-DR50.8 | 52.0 | ≤ 25.40 | 2.79 ± 0.41 | 17.3 ~ 51.5 Ø |
(RSFR-DR4.8-1.2)
Property | Test Method | Typical Value |
Tensile strength (MPa) | ASTM-D412 | ≥11.7 |
Tensile strength after ageing (MPa) | 150°C / 168h | ≥10.4 |
Tensile strength after fluid resistance (MPa) | AS23053/16 | ≥10.3 |
Elongation | ASTM-D412 | ≥400% |
Elongation at break after ageing | 150°C / 168h | ≥200% |
Elongation after fluid resistance | AS23053/16 | ≥200% |
Longitudinal shrink ratio | UL224 | + 10 |
Operating Temperature | IEC216 | -75°C to +150°C |
Full recovery Temperature | 200°C | |
Heat shock | 4hrs / 225°C | No cracking |
Flammability | ASTM-D2671 Procedure B | Pass |
Rated Voltage | 600V | |
Environment | RoHS Compliant | |
Dielectric Strength | ASTM-D2671 | ≥11.9kV/mm |
Shrink ratio | 2:1 | |
Standard | AMS-DTL-23053/16 | Pass |
SKU | RSFR-DR4.8-1.2 |
Brand | Radiform |